中文题名：工业硅渣浮选熔融分离提纯金属硅的实验研究

英文题名：EXPERIMENTAL STUDY OF SILICON SEPARATION FROM SLAG WITHIN THE CONCENTRATE ACQUIRED BY FLOTATION OF MGS REFINING SLAG USING SMELTING METHOD

作者：王家发 罗文波 周登凤 龙潇 麻红刚 罗达阳

第一作者：王家发

机构：[1]贵州理工学院材料与能源工程学院,贵州贵阳550003;[2]贵州雅友新材料有限公司,贵州瓮安550400

第一机构：贵州理工学院材料与能源工程学院

年份：2024

卷号：55

期号：2

起止页码：8-11

中文期刊名：铁合金

外文期刊名：Ferro-alloys

基金：贵州省基础研究计划(科学技术基金)资助项目(黔科合基础[2020]1Y221);贵州省贵州理工学院高层次人才科研启动资助项目(XJGC20190963)。

语种：中文

中文关键词：工业硅;硅渣;熔融;分离;提纯

外文关键词：metallurgical-grade silicon;silicon slag;smelting;separation;purification

摘要：介绍了使用工业硅渣浮选获得的工业硅粉,通过高温熔融法,分离残余渣相提纯工业硅,考察了不同气氛及熔剂添加量对渣-硅分离效果和工业硅杂质含量的影响。分别在空气气氛、氩气保护气氛及添加不同含量复合熔剂条件下,将10 g精矿样品于1450℃熔融处理5 min,随后淬冷制样磨抛统计样品单位截面积内硅滴的尺寸分布,以判断硅滴熔融聚集长大与渣相分离的特性。同时,检测不同条件下,熔融处理后获得的工业硅典型杂质含量变化。结果表明:惰性保护气氛会阻碍硅滴聚集长大与残余渣相分离,添加1%~2%的熔剂可加速硅滴长大集聚与渣相分离。在空气气氛并添加2%熔剂的条件下,可显著脱除熔融工业硅中的钙、铝杂质,可在一定程度上脱除部分铁、钛杂质。
In this study,silicon powder acquired via flotation of the refining slag of metallurgical grade silicon(MGS)was chosen as the basis of the experiments.High temperature smelting was adopted to separate silicon from the remaining slag.The effect of atmosphere and content of fusion agent addition on the separation of silicon from remaining slag were investigated.For each smelting experiment,10 g of powder sample was heated to 1450℃and held for 5 min under Ar protection or in air.The smelted samples were then mounted in resin and polished to show the cross-section and investigate the feature and size distribution of silicon drops within per unit area.Thus,the gathering and combining features of silicon drops and their separation process from slag can be evaluated.Meanwhile,impurity elements within the silicon drops before and after smelting under different circumstances were also measured.Results indicate:Ar protection can postpone the gathering and combining of silicon drops and deteriorate the separation of silicon from the slag.Adding 1%~2%of fusion agent can accelerate the gathering and separation of silicon from slag.Under the condition of air atmosphere and 2%fusion agent addition,Al and Ca in silicon can be removed obviously;Fe and Ti can be removed partially.